| PRODUCT NAME |
TYPE OF PRODUCT |
MgO |
Al2O3 |
Fe2O3 |
| MAGNESIA SPINEL BRICKS |
| MAGKOR-S20-LE |
Fired magnesia brick with low elastic modulus and high resistance to thermal shock. Favours coating development. |
81.0/85.0
|
11.0/15.0
|
<1.80
|
| MAGKOR-B |
Fired chromite ore free magnesia spinel refractory brick, volumetrically stable, low Fe2O3 and SiO2 content, with high resistance to thermal shock and redox atmosphere. |
83.0/87.0
|
11.0/15.0
|
<0.60
|
| MAGKOR-B-RA |
Fired chromite ore free magnesia spinel refarctory brick with high abrasion and clinker liquid phase corrosion resistance. |
92.0/93.0
|
5.0/8.0
|
<0.55
|
| MAGKOR-B-LP |
Fired magnesia spinel brick with a very low permeability to vapours, gases and clinker liquid phase infiltration. |
83.0/87.0
|
11.0/15.0
|
<0.50
|
| MAGKOR-B-LE |
Fired magnesia spinel brick with high resistance to thermal shock. Low elastic modulus |
85.5/92.5
|
6.0/9.0
|
<0.60
|
| MAGKOR-DB |
Special direct bonded brick, with high hot modulus of rupture. High resistance to cli8nker liquid phase corrosion indicated for kilns burning different alternative fuels with great variability |
83.0/87.0
|
10.5/13.5
|
<0.60
|
| MAGNESIA CHROME BRICKS |
| MAGNEFOR |
Magnesia-chrome refractory brick with high thermal shock resistance and excellent coatibility behaviour. |
79.0/83.0 |
<6.5 |
<5.00 |
| MAGNEFOR 60 |
Fired direct bonded magnesia chrome refractory brick, with high hot modulus of rupture. Indicated for sulphate resistant clinker. |
62.0/68.0 |
<11.0 |
<9.50 |
| MAGNEFOR 70 |
High fired magnesia chrome brick, volumetricallystable with high hot modulus of rupture and thermal shock resistance. |
67.0/74.0 |
max. 10.0 |
max. 9.0 |